1. Okulondoola ennyo enkola y'okusuula die .
The temperature of the aluminum water in the holding furnace should be controlled at ±3℃in order to stabilize the stirring temperature. The temperature after stirring must be adjusted according to the chemical composition of each furnace to ensure that the solid phase rate is stable at ±2%. The temperature of the mold must be checked and controlled so that the alloy can be smoothly filled and ordered to solidify. It is necessary to rationally formulate and adjust the process Parameters of the die casting machine mu budde, era okebere die castings okukakasa omutindo gwa die castings.
2, okwegendereza kw’omulimu gw’okufuuyira ekirungo ekifulumya .
Pay attention to how much the release agent coating is applied, avoid too much coating, too little or miss the coating. The parts where the castings are difficult to demold can be sprayed with more paint, and the parts that are easily released from the mold are less sprayed. When spraying the paint, use a spray gun to move from top to bottom, so that the water accumulated in the cavity flows from top to bottom, and the excess water is blown out of the cavity. The cavity is easy to stick to the mold part, and the first time is sprayed to cool down, and then sprayed to form a coating film. Do not get too close to the spray to prevent the paint water from flowing in the cavity. After spraying, use air to blow off the excess and accumulated paint in the cavity. In particular, pay attention to the paint in the deep cavity or dead Ensonda. Lirina okufuuwa okutangira amazzi okufuumuulwa mu bungi bwa ggaasi oluvannyuma lw’ebbugumu okubuguma, olwo okusuula n’eba n’obutuli. , okusuula wansi, okwawukana mu nnyonta, okufuumuuka, ekirina omulimu omukulu ennyo mu kumalawo okubeerawo kw’obutuli mu kusuula.
3. Okwegendereza nga okozesa firimu eyokya mu kyuma ekikuba ebifaananyi (die casting machine) .
Oluvannyuma lw’ekibumbe eky’ebbugumu eky’ekyuma ky’ebbugumu ly’ekibumbe okukozesebwa, ekibumbe ekyokya bwe kitandikibwa, ekirungo ky’amazzi kisobola okukozesebwa okubumba ekibumbe ekyokya 5-10 ekibumbe ku sipiidi entono, n’oluvannyuma aloy eya bulijjo eya semi-solid ne semi-solid die casting parameters zikozesebwa okukola die casting okukola, olwo ekibumbe kisobole okukuumibwa. kisobola n’okuziyiza okumyansa n’ebintu ebibuuka{{4} okubuuka {/}} okubuuka {4} okubuuka {4} okubuuka {4} okukebera okubuuka n’okubuuka {4} okubuuka {4} okubuuka {4} okusobola okubuuka. kisobola okutangira okufuuwa n’okubuuka {4}.